High Manganese Steel Wear Parts

Inquire Now

Concave-Mining Industry

  1) Material: Mn13Cr2, Mn18Cr2

               Mn20Cr2, Mn22Cr2

  2) Application: Gyratory Crusher

  3) Weight Range: 80-13,000 kgs

  4) Hardness: HB=190-230


Jaw Plate-Mining Industry

  1) Material: Mn13Cr2, Mn18Cr2

               Mn20Cr2, Mn22Cr2

  2) Application: Jaw Crusher

  3) Weight Range: 80-13,000 kgs

  4) Hardness: HB=190-230

Movable jaw plate of jaw crusher is also called jaw head or jaw back. And jaw plate is also called tooth plate, a vital wear resistant part of jaw crusher. A set of jaw plates usually are composed of movable jaw plate and fixed jaw plate. According to different models of jaw crushers, jaw plates also have the consistent sizes and models. In general, jaw plates are made of high-manganese steel.


Blow Bars-Cement Industry

  1) Material: Mn13Cr2, Mn18Cr2,

               Cr25, Cr27, Cr30

  2) Application: Impact Crusher

  3) Weight Range: 50-2,300 kgs

  4) Hardness: HB=190-230

                 HRC≥58


Track Shoe-Cement Industry

  1) Material: Mn13Cr2, Mn18Cr2

  2) Application: Excavator

  3) Unit Weight: 1.6 tons

  4) Hardness: HB=190-230

  5) Tensile strength: Min. 890mpa

  6) Yield strength: Min. 450mpa

  7) Area reduction: Min.30%

  8) Impact press: Min.190J/cm2


Hammer-Recycling Industry

  1) Material: Mn13, Mn13CrMo

  2) Application: Scrap Shredder

  3) Weight Range: 10-800 kgs

  4) Hardness: HB=190-230

 


Production Process


  • +86 731 8816 0991
  • +86 731 8816 0932
  • Building B25#-B26#, Liandong Jinyu Industrial Center, No. 308 section 2 of Maqiaohe Rd., Wangcheng Economic and Technological Development Zone, Changsha City, Hunan Province, P.R.China. 410200

Copyright © Hunan Hyster Material Technology Co., LTD. All Rights Reserved

Sitemap | Technical Support: